  2. SikaForce-335 GG, Self-leveling grout for glass panels, Interior & Exterior, Beige
SikaForce-335 GG, Self-leveling grout for glass panels, Interior & Exterior, Beige

SikaForce-335 GG, Self-leveling grout for glass panels, Interior & Exterior, Beige

Grouts
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17868/image_1920?unique=b734672
You have already submitted a query for this product today.
  • Packing

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 5 kg
Chemical Base Polyols - Isocyanate derivatives
Usage Structural adhesive for embedding glass panes in U-channels for railings
Usage Area Interior & Exterior
Color Beige
Working Time 30 minutes
Product Temperature 5 - 35 °C
Application Thickness N/A
Ambient Air Temperature +5 °C min. / +35 °C max.
Storage Conditions The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +10 °C and +30 °C
Density 1.5 g/cm3

Self-levelling 2-component PU-grout for embedding of glass panels

SikaForce®-335 GG is a pourable, self-levelling, two-component polymer grout based on polyurethane resin. It has been designed for embedding of monolithic or laminated glass panes in U-shaped support channels for standard glass railing, frameless or postless guard rail and balcony glazing. It is suitable for indoor and outdoor applications, if sealed with Sikasil® WS product.  

  • Stress-free glass embedding process
  • Allows homogenous load distribution
  • Long pot-life, easy to use
  • Room temperature curing
  • Solvent-free
PRODUCT BENEFITS
  • Stress-free glass embedding process
  • Allows homogenous load distribution
  • Long pot-life, easy to use
  • Room temperature curing
  • Solvent-free
 
Usage
SikaForce®-335 GG is designed for embedding of monolithic or laminated glass panes in U-shaped support channels for standard glass railing, frameless or postless guard rail and balcony glazing. It is suitable for indoor and outdoor applications, if sealed with Sikasil® WS product. This product is suitable for experienced professional users only. Test with actual substrates and conditions have to be performed to ensure material compatibility.  
Packaging

SikaForce®-335 GG Base Component

Can

5 kg

Pail25 kg

SikaForce®-010 Hardener

Can

1 kg

5 kg

 
Typical Product Data
Cure mechanism

Polyaddition
Mixing ratio by volumeby weight

100 : 25

100 : 19
Application temperature ambient

5 ─ 35 °C
Pot-life (CQP536-3)

30 minutes A
Shore D hardness (CQP023-1 / ISO 48-4)

60 B
Tensile strength (CQP036-2 / ISO527-2)

7.7 MPa B, C
Elongation at break (CQP036-2 / ISO 527-2)

20 % B, C
Glass transition temperature (ISO 11359-2)

5 °C D
SikaForce®-335 GGBase ComponentSikaForce®-010Hardener
Technical Information
CURE MECHANISM

The curing of SikaForce®-335 GG takes place by a chemical reaction of the two components. Higher temperatures speed up and lower slow down the curing process.

CHEMICAL RESISTANCE

In case of chemical or thermal exposure, conduct project related testing.
Application Information
METHOD OF APPLICATION

Consult the General Guideline “Glass Embedding” for construction details and dimensions prior to the product application.
Surface Preparation

Surfaces must be clean and dry.
Application

The procedure for manual application is as follows:
Stir the base part thoroughly until it is mixed homogeneously. Add the hardener in the specified ratio in the base part and stir until a homogeneous mixture is obtained. Apply before reaching half of the pot-life and join parts together within the open time. Consider that if mixed in bigger masses the exothermic reaction can influence the pot-life and open time significantly.
Prevent adhesion to glass with a release agent or bond breaker.
Removal

Uncured SikaForce®-335 GG may be removed from tools and equipment with Sika® Remover-208. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water. Do not use solvents on skin.

 
Application Limits

The compatibility of setting blocks, backer rods and other accessory materials in direct and indirect contact with SikaForce®-335 GG have to be approved by Sika in advance. It is recommended to use setting blocks made of SikaForce®-335 GG.
Avoid any stress caused by thermal dilatation.

The mechanical properties of SikaForce®-335 GG change depending on service temperature.

Impacts on glass and U-shaped support channel must be verified.
STORAGE CONDITIONS

SikaForce®-335 GG base component and SikaForce®-010 hardener have to be kept between 10 °C and 30 °C in a dry place. Do not expose it to direct sunlight or frost. After opening of the packaging, the content has to be protected against humidity.

Minimum temperature during transportation is -20 °C for max. 7 days.