Sika MonoTop-3400 Abraroc, High-strength, abrasion-resistant repair mortar, Interior & Exterior, Grey Powder, 25 kg

Category: Cement & Mortar

SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

This combination does not exist.

High Abrasion Resistant, High Strength Concrete Repair Mortar

Sika MonoTop-3400 Abraroc is a one-part, cementitious hand or machine applied, structural concrete repair mortar with very high resistance to hydraulic abrasion.

Ready to mix with water.
High abrasion resistance (A6 Classification).
High hydraulic abrasion resistance (equivalent to Granite).
Resistant to sea water and aggressive water conditions.
Applied up to 50 mm thick in one layer on vertical and horizontal applications.
Applied manually or mechanically (dry spray technique).

Usage

For new, and the refurbishment of, structures subject to hydraulic abrasion (sewer pipes, sewage treatment plants, dams, spillways, slipways, marine jetties and other maritime structures).
Water retaining structures containing water (pH > 4).
Abrasion resistant protective mortar layer.
Structures subjected to heavy abrasion or mechanical loads (storage or loading bays, silo floors, industrial floors, etc.).
Suitable for the environments XC1-XC4, XD1-XD3, XS1-XS3, XF1- XF4, XA1-XA3 according to the standard EN 206.
Restoration work (Principle 3, method 3.1 and 3.3 of EN 1504-9). Repair of spalling and damaged concrete in infrastructure and superstructure works.
Structural strengthening (Principle 4, method 4.4 of EN 1504-9). Increasing the bearing capacity of the concrete structure by adding mortar.
Preserving or restoring passivity (Principle 7, method 7,1 and 7,2 of EN 1504-9). Increasing cover with additional mortar and replacing contaminated or carbonated concrete.

Advantages

Ready to mix with water.
High abrasion resistance (A6 Classification).
High hydraulic abrasion resistance (equivalent to Granite).
Resistant to sea water and aggressive water conditions.
Applied up to 50 mm thick in one layer on vertical and horizontal applications.
Applied manually or mechanically (dry spray technique).

Packaging

25 kg bag

Colour

Grey powder

Technical Information

Abrasion Resistance

Wear Resistance Böhme

< 6 cm³/50 cm²

Wear Resistance

Material	Resistance Index
Sika MonoTop-3400 Abraroc	0,5–0,6 at 28 days
Granite	0,35–0,8 at 7 days
Glass	1 (reference)

1 Compagnie Nationale du Rhône test method for wet abrasion

Compressive Strength

1 day	2 days	7 days	28 days
~30 MPa	~45 MPa	~65 MPa	~85 MPa

C70	(EN 13892-2)

Modulus of Elasticity in Compression

≥ 20 GPa

(EN 13412)

Flexural Strength

1 day	2 days	7 days	28 days
~6 MPa	~7,5 MPa	~8,5 MPa	~11 MPa

F10	(EN 13892-2)

Tensile adhesion strength

≥ 2,0 MPa

(EN 1542)

Shrinkage

~500 µm/m at +20 °C 65 % relative humidity after 28 days

(EN 12617-4)

Restrained Shrinkage / Expansion

≥ 2,0 MPa

(EN 12617-4)

Thermal Compatibility

≥ 2,0 MPa (Part 1 Freeze-Thaw)

(EN 12687-1)

Capillary Absorption

≤ 0,5 kg·m^-2·h^-0,5

(EN 13057)

Water Penetration under Pressure

5 mm	(EN 12390-8 )

Carbonation Resistance

d_k ≤ control concrete (MC (0,45))

(EN 13295)

Reaction to Fire

Euroclass A1

(EN 13501-1)

Application Information

Mixing Ratio

2,75 litres of water for 25 kg powder.

Fresh mortar density

~2,25 kg/l

Layer Thickness

10 mm minimum / 50 mm maximum

Product Temperature

+5 °C minimum / +30 °C maximum

Ambient Air Temperature

+5 °C minimum / +30 °C maximum

Substrate Temperature

+5 °C minimum / +30 °C maximum

Application Time

+5 °C	+20 °C	+30 °C
~20 minutes	~15 minutes	~10 minutes

Waiting Time / Overcoating

Minimum 24 hours at 20 °C.

The above design is only a sample of the options available, for reference purposes only. Our policy of continuous improvement may result in a change of specifications without notice. If any discrepencies might be between the data sheet values and standards, we reserve the rights to make technical changes. Our company will not be held responsible, as all or any of pictures, drawings, weights and dimensions details or other elements in this document are only indicative and must not be considered contractual. Contact our sales team for other specifications or custom made products.

Contact our sales team for other specifications or custom made products.

Preview TDS

Download TDS

General Specifications
Packaging	25 kg
Usage	Abrasion-resistant mortar for hydraulic/marine/industrial structures
Usage Area	Interior & Exterior
Color	Grey powder
Chemical Base	Sulphate resistant cement, fibres, additives and selected abrasive resistant aggregates.
Storage Conditions	+5 °C to +35 °C - Store in original, unopened, undamaged packaging in dry conditions. Always refer to packaging
Density	2,25 kg/L
Application Thickness	10 mm >< 50 mm
Ambient Air Temperature	+5°C >< +30°C
Substrate Temperature	+5°C >< +30°C
Working time	N/A
Waiting Time	24 hours
Consumption	21 kg/m²/cm

High Abrasion Resistant, High Strength Concrete Repair Mortar

Sika MonoTop-3400 Abraroc is a one-part, cementitious hand or machine applied, structural concrete repair mortar with very high resistance to hydraulic abrasion.

Ready to mix with water.
High abrasion resistance (A6 Classification).
High hydraulic abrasion resistance (equivalent to Granite).
Resistant to sea water and aggressive water conditions.
Applied up to 50 mm thick in one layer on vertical and horizontal applications.
Applied manually or mechanically (dry spray technique).

Usage

For new, and the refurbishment of, structures subject to hydraulic abrasion (sewer pipes, sewage treatment plants, dams, spillways, slipways, marine jetties and other maritime structures).
Water retaining structures containing water (pH > 4).
Abrasion resistant protective mortar layer.
Structures subjected to heavy abrasion or mechanical loads (storage or loading bays, silo floors, industrial floors, etc.).
Suitable for the environments XC1-XC4, XD1-XD3, XS1-XS3, XF1- XF4, XA1-XA3 according to the standard EN 206.
Restoration work (Principle 3, method 3.1 and 3.3 of EN 1504-9). Repair of spalling and damaged concrete in infrastructure and superstructure works.
Structural strengthening (Principle 4, method 4.4 of EN 1504-9). Increasing the bearing capacity of the concrete structure by adding mortar.
Preserving or restoring passivity (Principle 7, method 7,1 and 7,2 of EN 1504-9). Increasing cover with additional mortar and replacing contaminated or carbonated concrete.

Advantages

Ready to mix with water.
High abrasion resistance (A6 Classification).
High hydraulic abrasion resistance (equivalent to Granite).
Resistant to sea water and aggressive water conditions.
Applied up to 50 mm thick in one layer on vertical and horizontal applications.
Applied manually or mechanically (dry spray technique).

Packaging

25 kg bag

Colour

Grey powder

Technical Information

Abrasion Resistance

Wear Resistance Böhme

< 6 cm³/50 cm²

Wear Resistance

Material	Resistance Index
Sika MonoTop-3400 Abraroc	0,5–0,6 at 28 days
Granite	0,35–0,8 at 7 days
Glass	1 (reference)

1 Compagnie Nationale du Rhône test method for wet abrasion

Compressive Strength

1 day	2 days	7 days	28 days
~30 MPa	~45 MPa	~65 MPa	~85 MPa

C70	(EN 13892-2)

Modulus of Elasticity in Compression

≥ 20 GPa

(EN 13412)

Flexural Strength

1 day	2 days	7 days	28 days
~6 MPa	~7,5 MPa	~8,5 MPa	~11 MPa

F10	(EN 13892-2)

Tensile adhesion strength

≥ 2,0 MPa

(EN 1542)

Shrinkage

~500 µm/m at +20 °C 65 % relative humidity after 28 days

(EN 12617-4)

Restrained Shrinkage / Expansion

≥ 2,0 MPa

(EN 12617-4)

Thermal Compatibility

≥ 2,0 MPa (Part 1 Freeze-Thaw)

(EN 12687-1)

Capillary Absorption

≤ 0,5 kg·m^-2·h^-0,5

(EN 13057)

Water Penetration under Pressure

5 mm	(EN 12390-8 )

Carbonation Resistance

d_k ≤ control concrete (MC (0,45))

(EN 13295)

Reaction to Fire

Euroclass A1

(EN 13501-1)

Application Information

Mixing Ratio

2,75 litres of water for 25 kg powder.

Fresh mortar density

~2,25 kg/l

Layer Thickness

10 mm minimum / 50 mm maximum

Product Temperature

+5 °C minimum / +30 °C maximum

Ambient Air Temperature

+5 °C minimum / +30 °C maximum

Substrate Temperature

+5 °C minimum / +30 °C maximum

Application Time

+5 °C	+20 °C	+30 °C
~20 minutes	~15 minutes	~10 minutes

Waiting Time / Overcoating

Minimum 24 hours at 20 °C.