  2. Sikasil SG-550, 2-Component Silicone for Structural Glazing, Exterior, Black
Sikasil SG-550, 2-Component Silicone for Structural Glazing, Exterior, Black

Sikasil SG-550, 2-Component Silicone for Structural Glazing, Exterior, Black

Adhesives & Sealants
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17381/image_1920?unique=b734672
You have already submitted a query for this product today.
  • Packing

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 20 kg
Usage Structural Glazing With Silicone
Usage Area Exterior
Color Black
Chemical Base 2-component silicone
Storage Conditions N/A
Density 1.3 kg/L
Service Temperature -40 >< +150
Application Time 10 - 15 min.
Curing Time 24 hours
Application Thickness 2 >< 3 mm
Application Method Gun
UV Resistant Yes
Moisture Resistant Yes
Mold Resistant No
Paintable No
Sealant Yes
Flexible Yes

High-strength, 2-component silicone structural glazing adhesive, CE-marked

Sikasil SG-550 is a 2-component, neutral-curing structural silicone adhesive with very high mechanical strength. It is mainly used for structural glazing applications and is well suited wherever in structural bonding higher mechanical strength is required. It is complying with EOTA ETAG 002 and provided with the CE-mark.  

  • Meets requirements of EOTA ETAG 002
    (carries ETA), EN 15434, ASTM C1184 and
    ASTM C920 (class 12.5, movement capability ± 12.5 %)
  • Structural Sealant Glazing Kit: Structural Sealant according ETAG 002 Part 1 Edition November 1999 (Revised March 2012) used as EAD, ETA-11/0392 issued by Technical Assessment Body Österreichisches Institut für Bautechnik, Declaration of Performance 60241468, certified by notified product certification body 0757, certificate of constancy of performance 0757-CPR-596-7110760-5-4, and provided with the CE marking
  • High design tensile strength for dynamic loads: σ des = 0.20 MPa (ETA)
  • SNJF-VEC recognized (product code: 3741)
  • Outstanding UV and weathering resistance
PRODUCT BENEFITS
  • Meets requirements of EOTA ETAG 002
    (carries ETA), EN 15434, ASTM C1184 and
    ASTM C920 (class 12.5, movement capability ± 12.5 %)
  • Structural Sealant Glazing Kit: Structural Sealant according ETAG 002 Part 1 Edition November 1999 (Revised March 2012) used as EAD, ETA-11/0392 issued by Technical Assessment Body Österreichisches Institut für Bautechnik, Declaration of Performance 60241468, certified by notified product certification body 0757, certificate of constancy of performance 0757-CPR-596-7110760-5-4, and provided with the CE marking
  • High design tensile strength for dynamic loads: σdes = 0.20 MPa (ETA)

  • SNJF-VEC recognized (product code: 3741)

  • Outstanding UV and weathering resistance
 
Usage
Sikasil SG-550 is ideal for structural glazing and other bonding applications where high mechanical strength with silicone is required. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.  
Packaging

Sikasil SG-550 (A)

Pail

25 kg

Drum250 kg

Sikasil SG-550 (B)

Pail

20 kg
Typical Product Data
Chemical base

2-component silicone

Cure mechanism

Polycondensation

Cure type

Neutral

Mixing ratioA:B by volumeA:B by weight

10:1

12:1

Consistency

Paste

Application temperatureambient

5 ─ 40 °C

Snap time (CQP554-1)

30 minutes A

Tack free time (CQP019-3)

150 minutes A

Shore A hardness (CQP023-1 / ISO 48-4)

55

Tensile strength (CQP036-1 / ISO 527)

3.4 MPa

100 % modulus (CQP036-1 / ISO 527)

1.7 MPa

Elongation at break (CQP036-1 / ISO 527)

300 %

Tear propagation resistance (CQP045-1 / ISO 34)

4.5 N/mm

Service temperature (CQP513-1)

-40 ─ 150 °C

Sikasil SG-550 (A)Sikasil SG-550 (B)
Technical Information
CURE MECHANISM

Sikasil SG-550 starts to cure immediately after mixing the two components.
The speed of the reaction depends mainly on the temperature, i.e. the higher the temperature the faster the curing process. Heating above 50 °C could lead to bubble formation and is therefore not allowed.
The mixer open time, i. e. the time the material can remain in the mixer without flushing or extrusion of product, is significantly shorter than the snap time indicated above.
Application Information
Surface Preparation

Surfaces must be clean, dry and free from grease, oil and dust. Surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond.
Application

The optimum temperature for substrate and sealant is between 15 °C and 25 °C.

Before processing Sikasil SG-550 both components have to be mixed homogeneously and air-bubble-free in the correct ratio as indicated with an accuracy of ± 10 %. For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.
Consider that the B-component is moisture-sensitive and must therefore only be exposed briefly to air.
Joints must be properly dimensioned.

Basis for calculation of the necessary joint dimensions are the technical values of the adhesive and the adjacent building materials, the exposure of the building elements, their construction and size as well as external loads.
Tooling and finishing

Tooling and finishing must be carried out within the snap time of the adhesive.

When tooling freshly applied Sikasil SG-550, press the adhesive to the joint flanks to get a good wetting of the bonding surface. No tooling agents must be used.

 
Removal

Uncured Sikasil SG-550 may be removed from tools and equipment with Sika Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.

Re-usable, usually metallic, static mixer can be cleaned with Sika Mixer Cleaner.

Hands and exposed skin have to be washed immediately using hand wipes such as Sika Cleaner-350H cleaning towels or a suitable industrial hand cleaner and water. Do not use solvents on skin.
Overpainting

Sikasil SG-550 cannot be overpainted.
Application Limits

Recommended solution from Sika for structural glazing and window bonding are usually compatible to each other. These solutions consist of products such as Sikasil SG, IG, WS and WT series. For specific information regarding compatibility between various Sikasil products and other Sika products contact the Technical Department of Sika Industry.
To exclude materials influencing Sikasil SG-550, all materials such as gaskets, setting blocks, sealants etc., in direct and indirect contact have to be approved by Sika in advance.
Where two or more different reactive sealants are used, allow the first to cure completely before applying the next one.
The above mentioned Sika process materials may only be used in structural glazing or window bonding applications after a detailed examination and written approval of the corresponding project details by Sika Industry.