  2. SikaPower-1200, Fast Curing High Strength Assembly Adhesive, Interior & Exterior, Green
SikaPower-1200, Fast Curing High Strength Assembly Adhesive, Interior & Exterior, Green

SikaPower-1200, Fast Curing High Strength Assembly Adhesive, Interior & Exterior, Green

Adhesives & Sealants
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17616/image_1920?unique=b734672
You have already submitted a query for this product today.
  • Packing

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 220 kg + 240 kg
Usage High-Strength Bonding Of Stressed Components
Usage Area Interior & Exterior
Color Green
Chemical Base Epoxy - Amine
Storage Conditions +10 °C to +35 °C - Store in original, unopened, undamaged packaging in dry conditions. Always refer to packaging.
Density 1.18 g/cm3
Service Temperature N/A
Application Time 45 min.
Curing Time 48 hours
Application Thickness 3 mm
Application Method Manual / cartridge
UV Resistant No
Moisture Resistant Yes
Mold Resistant N/A
Paintable No
Sealant No
Flexible Yes

Fast curing, tough and high strength assembly adhesive

SikaPower-1200 is a tough, high strength, solvent free, thixotropic, fast curing epoxy adhesive. It is designed for fast assembly bonding of structural composite substrates, like GFRP and CFRP laminates, as well as metallic substrates. The adhesive cures by polyaddition of the two components.  

  • High fatigue and impact resistance
  • Long open time at high temperature and humidity
  • Cures at room temperature
  • Accelerated curing and higher mechanical strength with heat
  • Good adhesion to fibre-reinforced plastics
  • Does not contain solvents or PVC
PRODUCT BENEFITS
  • High fatigue and impact resistance
  • Long open time at high temperature and humidity
  • Cures at room temperature
  • Accelerated curing and higher mechanical strength with heat
  • Good adhesion to fibre-reinforced plastics
  • Does not contain solvents or PVC

 
Usage
SikaPower-1200 is suitable for fast assembly bonding of highly stressed components, especially if high strength and high fatigue properties are required.
This product is suitable for professional experienced users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.  
Packaging

SikaPower-1200 (A)

Drum

220 kg

SikaPower-1040 (B)

Drum

240 kg

SikaPower-1200 (A+B)

Cartridge

400 ml

Mixer: Sulzer MixPacTM MFH 10-24T

Cartridge

450 ml

Mixer: Sulzer MixPacTM MGQ 08-24T

 
Typical Product Data
Mixing ratioA:B by volumeA:B by weight

100:50

100:54

Solid content

100 %

Consistency

Thixotropic paste

Application temperature

15 ─ 30 °C

Open time (CQP046-11 / ISO 4587)

45 min B, C, D

Curing time (CQP046-9, ISO4587)at 23 °Cat 70 °C

48 hours

2 hours

Tensile strength (CQP543-1 / ISO 527)

40 MPa C, E

E-Modulus (CQP543-1 / ISO 527)

2600 MPa C, E

Elongation at break (CQP543-1 / ISO 527)

3.5 % C, E

Tensile lap-shear strength (CQP046-9 / ISO 4587)

20 MPa C, D, E

Critical stress intensity factor KIc (ISO 13586)

2.7 m1/2 MPa C, E, F

Critical energy release rate GIc (ISO 13586)

3.5 N/mm C, E, F

Glass transition temperature (CQP509-1 / ISO 6721)

90 °C E

Shelf lifedrumcartridges

12 months  G

24 months  G

Component ASikaPower-1200Component BSikaPower-1040
Technical Information
CURE MECHANISM

SikaPower-1200 cures by chemical reaction of the two components at room temperature. Higher temperatures speed up the curing process and lower temperatures slow down the curing process. The final glass transition temperature, as well as the tensile and shear strengths, may be increased with higher curing temperature.

CHEMICAL RESISTANCE

In view of potential chemical or thermal exposure, it is required to conduct a project related testing.
Application Information
Surface Preparation

SikaPower-1200 adheres usually well to fiber-reinforced plastics if applied subsequently after the removal of the protective peel ply.

Surfaces must be clean, dry and free from grease, oil and dust. Surface treatment may be required depending on the specific nature of the substrates. All pre-treatment steps must be confirmed by preliminary tests on original substrates considering specific conditions in the assembly process.
Application

SikaPower-1200 is dispensed from dual cartridges with adequate manual or pneumatic guns. Extrude adhesive without mixer to equalize the filling levels. Attach the mixer and dispose of the first few cm of the bead before the application.

For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.

 
Removal

Uncured SikaPower-1200 may be removed from tools and equipment with Sika Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika Cleaner-350H cleaning towels or a suitable industrial hand cleaner and water.

Do not use solvents on skin.
STORAGE CONDITIONS

SikaPower-1200 has to be stored between 10 °C and 35 °C in a dry place. Do not expose to direct sunlight of frost. After opening of the packaging, the contents have to be protected against humidity.