SikaFlex 111 Stick&Seal, Adeziv hibrid, 290ml
SIKA
Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.
Read moreFlexible adhesive and sealant Sikaflex®-111 Stick & Seal is a 1-part, multipurpose adhesive and sealant with a very broad adhesion and sealing profile which bonds and seals most construction material substrates. Internal and external use. | |||||||||||||||||||||||||||||||||||||||
UsageAn adhesive to bond most construction components and materials such as:
A sealant to seal vertical and horizontal joints. Advantages
Packaging290 ml cartridge, 12 cartridges per box ColourWhite, Concrete Grey, Black | |||||||||||||||||||||||||||||||||||||||
Typical Product Data
| |||||||||||||||||||||||||||||||||||||||
ApplicationSag flow
Ambient air temperature +5 °C (+41 °F) min. / +40 °C (+104 °F) max. Substrate temperature +5 °C (+41 °F) min. / +40 °C (+104 °F) max., min. 3 °C (37 °F) above dew point temperature Backing material Use closed cell, polyethylene foam backing rods Curing rate
Skinning time
Yield
SUBSTRATE PREPARATION The substrate must be sound, clean, dry and free of all contaminants such as dirt, oil, grease, cement laitance, old sealants and poorly bonded paint coatings which could affect adhesion of the adhesive / sealant. The substrate should be of sufficient strength to resist with the stresses induced by the sealant during movement. Removal techniques such as wire brushing, grinding, sanding or other suitable mechanical tools can be used. All dust, loose and friable material must be completely removed from all surfaces before application of any activators, primers or adhesive / sealant. Sikaflex®-111 Stick & Seal adheres without primers and/or activators. However, for optimum adhesion, joint durability and critical, high performance applications the following priming and/or pre-treatment procedures shall be followed: Non-porous substrates Aluminium, anodised aluminium, stainless steel, galvanised steel, powder coated metals, glazed tiles or PVC: slightly roughen surface with a fine abrasive pad. Clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth. Before bonding / sealing, allow a waiting time of > 15 minutes (< 6 hours). Other metals, such as copper, brass and titanium-zinc: clean and pre-treat using Sika® Cleaner P or Sika® Aktivator-205 applied with a clean cloth. After a waiting time of > 15 minutes (< 6 hours). Apply Sika® Primer-3 N applied by brush. Allow a further waiting time of > 30 minutes (< 8 hours) before bonding / sealing. Porous substrates Concrete, aerated concrete and cement-based renders, mortars and bricks: prime surface using Sika® Primer-3 N applied by brush. Before bonding / sealing, allow a waiting time of > 30 minutes (< 8 hours). For more detailed advice and instructions contact Sika Technical Services. Note: Primers are adhesion promoters and not an alternative to improve poor preparation / cleaning of joint surfaces. Primers also improve the long-term adhesion performance of the sealed joint. CLEANING OF EQUIPMENT Clean all tools and application equipment immediately after use with Sika® Remover-208. Once cured, hardened material can only be removed mechanically. For cleaning skin use Sika® Cleaning Wipes. |