Sikalastic-625 BMS, Low Co2 Footprint Polyurethane Liquid Waterproofing, Exterior, 15 L
SIKA
Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.
Read more| High performance reduced CO2 footprint polyurethane liquid applied waterproofing Sikalastic®-625 BMS is a 1-part polyurethane, reinforced, cold-applied liquid membrane. It provides a flexible, seamless waterproofing solution using Sika's unique i-Cure technology and selected sustainable raw materials derived from renewable sources, thereby reducing the product's carbon footprint.
| ||||||||||||||||||||
UsageDesigned for the following waterproofing applications:
Advantages
Packaging15 L container Refer to current price list for packaging variations. ColourNote: Applied colours selected from colour charts will be approximate. Note: For colour matching: Apply colour sample and confirm selected colour under real lighting conditions. Light Grey and Dark Grey | ||||||||||||||||||||
Technical Information Tensile Strength Reinforced ~14 N/mm2 Unreinforced ~8 N/mm2 Tear Strength ~36 N/mm (ISO 527-1/3) Service Temperature -30 °C min. / +90 °C max. Thermal Resistance -20 °C min. / +80 °C max. Chemical Resistance Resistant to many chemicals. Contact Sika Technical Services for additional information. External Fire Performance Broof (T1), Broof (T4) Dry film thickness Waterproofing kit for all flat roof types ~1,5 mm | ||||||||||||||||||||
Application Information Ambient Air Temperature +5 °C min. / +40 °C max. Relative Air Humidity 20 % min. / 85 % max. Dew Point Beware of condensation. The substrate and uncured applied product must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the surface of the applied product. Metal surfaces will be more prone to temperature fluctuations occurring and wind chill effects. Substrate Temperature +5 °C min. / +60 °C max. Substrate Moisture Content ≤ 4% parts by weight The following test methods can be used to determine the substrate moisture content:
Pot Life Note: The material in opened containers must be applied before a surface skin occurs. Note: Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity. ~1–2 hours Applied Product Ready for Use Important: The impact of heavy rain or rain showers can physically mark or damage the membrane in its liquid state. Note: Application at higher than recommended film thicknesses may result in a prolonged “soft” feel to the coating. This will eventually cure and harden. Note: Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
|