| Sikagard®-406 W is a single component white, waterborne acrylic resin based surface coating containing an organic in film preservative with a mat finish. - Easy to apply
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good covering and hiding power (opacity)
- Permeable to water vapour
- Ultra-low emission
- More flexible in comparison to standard paints, improved resistance to cracking and flaking
- Mat finish
- Seamless, easy to clean finish
- Low odour
|
Usage - Top coat or standalone coating for internal walls and ceilings
- For concrete, bricks, cement based and gypsum substrates, metallic surfaces, timber, tiles and plastic
- Suitable for pharmaceutical, medical engineering, food and beverage industry, hospitals, healthcare facilities, kitchens and prisons and leisure facilities
Advantages - Easy to apply
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good covering and hiding power (opacity)
- Permeable to water vapour
- Ultra-low emission
- More flexible in comparison to standard paints, improved resistance to cracking and flaking
- Mat finish
- Seamless, easy to clean finish
- Low odour
Packaging 5.0 l (= 6.60kg) drums 15.0 l (= 19.80 kg) containers Colour Available colours BS08B15, BS12B21, BS14C31, BS18E49, BS18E50, RAL1013, RAL3015, RAL7035, RAL9001, White |
Technical Information Tensile Strength ~10 N/mm² unreinforced | (EN ISO 527-3) |
Tensile adhesion strength | > 1.5N/mm² | to concrete using Sika Bonding Primer |
Chemical Resistance Good short-term resistance to weak acids, alkalis and cleaning products. Please contact Sika technical service for specific information. Disinfection with Hydrogen Peroxide Vapour: - Resistant when using Steris VHP technology
- Resistant to PEA vaporisation technology, when a system build up with glass fibre reinforcement is used
- Resistant when using Oxypharm vaporiser type Nocospray under following conditions:
| Disinfectant | Concentration | Setting at vaporiser | Contact time | | NOCOLYSE Mint (6 %) | 1 ml/m³ | 20 m³
(1.5 minutes vaporisation) | 30 min | | NOCOLYSE One Shot (12 %) | 3 ml/m³ (2 cycles) | 45m³
(5 minutes vaporisation) | 30 min | | NOCOLYSE Food (7.9 %) | 1 ml/m³ | 20 m³
(1.5 minutes vaporisation) | 30 min | | NOCOLYSE Food (7.9 %) | 5 ml/m³ (2 cycles) | 75m³
(5 minutes vaporisation) | 60 min |
|
Application Information Ambient Air Temperature +8°C min. / +35°C max. Relative Air Humidity < 80% Dew Point Beware of condensation!
The substrate must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the wall finish. Substrate Temperature +8 °C min. / +35 °C max. Substrate Moisture Content Visible damp free, < 6 % pbw moisture content test method: Sika®-Tramex meter Curing Time Before applying Sikagard®-406 W to Sikagard®-406 W allow: Substrate temperature | Minimum | Maximum | +10 °C | 4 hours | 7 days | +20 °C | 2 hours | 7 days | +30 °C | 1 hour | 7 days |
Before applying Sikagard®-406 W to Sikagard®-403 W allow: Substrate temperature | Minimum | Maximum | +10 °C | 4 hours | 7 days | +20 °C | 1 hour | 7 days | +30 °C | 1 hour | 7 days |
Applied Product Ready for Use Temperature | Tack free | Full cure | +10 °C/ 50 % r.h. | ~ 8 hours | ~ 7days | +20 °C/ 50 % r.h. | ~ 4 hours | ~ 7days | +30 °C/ 50 % r.h. | ~ 3 hours | ~ 7days |
|
The above design is only a sample of the options available, for reference purposes only. Our policy of continuous improvement may result in a change of specifications without notice. If any discrepencies might be between the data sheet values and standards, we reserve the rights to make technical changes. Our company will not be held responsible, as all or any of pictures, drawings, weights and dimensions details or other elements in this document are only indicative and must not be considered contractual. Contact our sales team for other specifications or custom made products.
Contact our sales team for other specifications or custom made products.