  2. Sikacor Eg-5, 2-Component Polyurethane Top Coat for Industrial Floors
Sikacor Eg-5, 2-Component Polyurethane Top Coat for Industrial Floors

Sikacor Eg-5, 2-Component Polyurethane Top Coat for Industrial Floors

Rășini
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/18097/image_1920?unique=b734672
You have already submitted a query for this product today.
  • Color
  • Packing

Această combinație nu există.

Contactați-ne
Preview TDS
Download TDS
General Specifications
Ambalaj SikaCor EG-5: 3 kg; Sika Thinner EG: 10 L and 3 L; SikaCor Cleaner: 25 L
Baza chimică Polyurethane
Utilizare Topcoat for corrosion protection and line marking on resin floors
Metoda de aplicare Airless spray or brush/roller
Zona de utilizare Exterior
Culoare RAL 1023
Temperatura aerului ambiant +5 °C min.
Condiții de depozitare In originally sealed containers in a cool and dry environment
Timp de întărire N/A
Timp de lucru At + 10°C ~7 h; At + 20°C ~5 h; At + 30°C ~4 h
Densitate 1.3 kg/L
Consum 0.130 kg/m²

2-pack AY-PUR top coat

SikaCor EG-5 is a 2-pack acrylic polyurethane top coat. By adding 1 % b.w. SikaCor PUR Accelerator (see product data sheet for more information) a fast touch and through drying will be achieved.

  • Very good corrosion protection properties
  • Tough elastic and hard but not brittle
  • Largely insensitive against shock and impact
  • Excellent chemical, weather and colour stability
Usage
In combination with 2-pack primer and intermediate coats of the SikaCor and Sika Permacor product range for heavy duty corrosion protection of atmospheric exposed and submerged steel structures. SikaCor EG-5 can also be used as a line marking paint on selflevelling and broadcasted epoxy and polyurethan resin based floors e. g. for car parks.  
Advantages
  • Very good corrosion protection properties
  • Tough elastic and hard but not brittle
  • Largely insensitive against shock and impact
  • Excellent chemical, weather and colour stability
Packaging
SikaCor EG-53 kg and 10 kg net.
Sika Thinner EG10 l and 3 l
SikaCor Cleaner25 l
Colour

Available colours: RAL 1023, RAL 3020, RAL 5010, RAL 6029, RAL 7011, RAL 7036, RAL 7037, RAL 7038, RAL 9005
Technical Information
Chemical Resistance

Weather, water, sewage, seawater, smoke, de-icing salts, acid and lye vapours, oils, grease and short term exposure to fuels and solvents.

Thermal Resistance

Dry heat up to + 150°C, short term up to + 200°C
Damp heat up to approx. + 50°C
In case of higher temperatures please consult Sika.

An exposure to high temperatures can lead to color changes.
Application Information
Mixing Ratio

Components A : B

By weight

90 : 10

By volume7.1 : 1*

*The volumetric mixing ratio may vary depending on the colour shade. Please refer to Sika, if needed.
Thinner

Sika Thinner EG
If necessary max. 5% Sika Thinner EG may be added to adapt the viscosity.
Product Temperature

Min. + 5°C
Relative Air Humidity

Max. 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point.

The surface must be dry and free from ice.
Surface temperature

Min. + 5°C
0°C by adding SikaCor PUR Accelerator
Pot Life

At + 10°C

~7 h

~5 h *

At + 20°C

~5 h

~3 h *

At + 30°C

~4 h

~2 h *

* By adding 1 % b.w. SikaCor PUR Accelerator
Drying stage 6
Dry film thickness 80 μm

+ 5°C after

21 h

+ 10°C after18 h
+ 20°C after

14 h

+ 40°C after3 h
+ 80°C after45 min

By adding 1 % b.w. SikaCor PUR Accelerator:

Dry film thickness 80 μm

0°C after

52 h

+ 5°C after18 h
+ 10°C after13 h
+ 20°C after5 h
Waiting Time / Overcoating

Min. until drying stage 6 is achieved

Max. unlimited

Prior to further applications possible contamination must be removed.
Drying time

Final drying time
Depending on film thickness and temperature full hardness is achieved after 1 - 2 weeks. Tests of the completed coating system should only be carried out after final curing.