| SikaCor EG-5 is a 2-pack acrylic polyurethane top coat. By adding 1 % b.w. SikaCor PUR Accelerator (see product data sheet for more information) a fast touch and through drying will be achieved. - Very good corrosion protection properties
- Tough elastic and hard but not brittle
- Largely insensitive against shock and impact
- Excellent chemical, weather and colour stability
|
Usage In combination with 2-pack primer and intermediate coats of the SikaCor and Sika Permacor product range for heavy duty corrosion protection of atmospheric exposed and submerged steel structures. SikaCor EG-5 can also be used as a line marking paint on selflevelling and broadcasted epoxy and polyurethan resin based floors e. g. for car parks. Advantages - Very good corrosion protection properties
- Tough elastic and hard but not brittle
- Largely insensitive against shock and impact
- Excellent chemical, weather and colour stability
Packaging | SikaCor EG-5 | 3 kg and 10 kg net. | | Sika Thinner EG | 10 l and 3 l | | SikaCor Cleaner | 25 l |
Colour Available colours: RAL 1023, RAL 3020, RAL 5010, RAL 6029, RAL 7011, RAL 7036, RAL 7037, RAL 7038, RAL 9005 |
Technical Information Chemical Resistance Weather, water, sewage, seawater, smoke, de-icing salts, acid and lye vapours, oils, grease and short term exposure to fuels and solvents.
Thermal Resistance Dry heat up to + 150°C, short term up to + 200°C
Damp heat up to approx. + 50°C
In case of higher temperatures please consult Sika. An exposure to high temperatures can lead to color changes.
|
Application Information Mixing Ratio | By weight | 90 : 10 | | By volume | 7.1 : 1* |
*The volumetric mixing ratio may vary depending on the colour shade. Please refer to Sika, if needed. Thinner Sika Thinner EG
If necessary max. 5% Sika Thinner EG may be added to adapt the viscosity. Product Temperature Min. + 5°C Relative Air Humidity Max. 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point. The surface must be dry and free from ice. Surface temperature Min. + 5°C
0°C by adding SikaCor PUR Accelerator Pot Life | At + 10°C | ~7 h | ~5 h * | | At + 20°C | ~5 h | ~3 h * | | At + 30°C | ~4 h | ~2 h * |
* By adding 1 % b.w. SikaCor PUR Accelerator Drying stage 6 | Dry film thickness 80 μm | | + 5°C after | 21 h | | + 10°C after | 18 h | | + 20°C after | 14 h | | + 40°C after | 3 h | | + 80°C after | 45 min |
By adding 1 % b.w. SikaCor PUR Accelerator: | | Dry film thickness 80 μm | | 0°C after | 52 h | | + 5°C after | 18 h | | + 10°C after | 13 h | | + 20°C after | 5 h |
Waiting Time / Overcoating Min. until drying stage 6 is achieved Max. unlimited Prior to further applications possible contamination must be removed. Drying time Final drying time
Depending on film thickness and temperature full hardness is achieved after 1 - 2 weeks. Tests of the completed coating system should only be carried out after final curing. |
The above design is only a sample of the options available, for reference purposes only. Our policy of continuous improvement may result in a change of specifications without notice. If any discrepencies might be between the data sheet values and standards, we reserve the rights to make technical changes. Our company will not be held responsible, as all or any of pictures, drawings, weights and dimensions details or other elements in this document are only indicative and must not be considered contractual. Contact our sales team for other specifications or custom made products.