  2. Sika Armorex L2 High Flow, High-flow, fast-setting grout, Interior & Exterior, Grey, 25 kg
Sika Armorex L2 High Flow, High-flow, fast-setting grout, Interior & Exterior, Grey, 25 kg

Sika Armorex L2 High Flow, High-flow, fast-setting grout, Interior & Exterior, Grey, 25 kg

Grouts
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17862/image_1920?unique=ab4a244
You have already submitted a query for this product today.

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 25 kg
Chemical Base Cement, selected fillers and aggregates, special additives
Usage High performance grouting for machine bases, precast concrete, repairs (10-100mm)
Usage Area Interior & Exterior
Color Grey
Working Time N/A
Product Temperature 15 - 20 °C
Application Thickness 10 mm >< 100 mm
Ambient Air Temperature +5 °C min. / +25 °C max.
Storage Conditions Store properly in dry conditions in undamaged and unopened original sealed packaging
Density 2180 kg/m³

High Flow Rapid Strength Grout

Sika® Armorex® L2 High Flow is a one part, high flow, rapid strength cementitious grout.

  • High strength
  • Shrinkage compensated
  • High flowability retention
  • Durable
  • Non metallic
  • Impressive track record
  • Quality assured factory blend
  • Chloride free
  • >40 N/mm2 in 24 hours
Usage
  • For precision, high performance, grouting underneath machine bases, structural steelwork, etc
  • For grouting precast concrete units and anchor bars
  • Repairing concrete structures
  • Filling voids
  • For grouting thicknesses between 10 -100 mm
  • Steel reinforcement anchoring
 
Advantages
  • High strength
  • Shrinkage compensated
  • High flowability retention
  • Durable
  • Non metallic
  • Impressive track record
  • Quality assured factory blend
  • Chloride free
  • >40 N/mm2 in 24 hours
Packaging

25kg bags
Colour

Grey powder
Technical Information
Compressive Strength

Compressive Strength tested to BS 1881:Part 116:1983 - ambient temperature +20°C

1 day

3 days

7 days

28 days

Pourable

~42MPa

~56MPa

~68MPa

~77MPa

Flowable

~40MPa

~54MPa

~65MPa

~74MPa

Fluid~25MPa~45MPa~60MPa~70MPa

Modulus of Elasticity in Compression

~29 GPa

Flexural Strength

7 days

28 days

~8MPa

~10.5MPa

Ambient temperature +20°C

Tensile Strength

7 days

28 days

~2MPa

~3.5MPa

Ambient temperature +20°C

Pull-Out Resistance

Pull out (Dry)

Displacement < 0.6mm at load of 75KN (BS EN 1504-6)

Pull out (Wet)

Displacement < 0.6mm at load of 75KN (BS EN 1504 -6)

Ultimate Anchorage Bond Strength

6.7 MPa

Electrical Resistivity

~4.5 (K.ohm.cm)

(Wenner Test)
Application Information
Layer Thickness

10 mm min. / 100mm max
Flowability

Flow cone test

5°C

33 seconds

20°C

33 seconds

Efflux times at fluid consistency
Ambient Air Temperature

+5°C min. / +25°C max.
Substrate Temperature

+5°C min. / +25°C max.