Two component, PMMA based, filler compound
Sikalastic® Rapid Filler Compound is a fast-reactive and flexible product used to fill small cracks and joints as well as to smooth out areas of minor unevenness. It is used mainly to prepare the substrate before PMMA waterproofing and surfacing systems are applied. The product can also be used to smooth out fleece overlaps in the waterproofing layer.
-
Fast curing
-
Easy and fast application
-
Solvent free
-
Hydrolysis and alkali-resistant
|
Usage
- Filler for small cracks and joints for prior to application of Sikalastic® Rapid systems.
Advantages
- Fast curing
- Easy and fast application
- Solvent free
- Hydrolysis and alkali-resistant
Packaging
| SUMMER | | | Sikalastic® Rapid Filler Compound | 10.00kg | | Sikalastic® Rapid Catalyst | 0.30kg (3 x 0.1kg) | | Total | 10.30kg |
| WINTER | | | Sikalastic® Rapid Filler Compound | 10.00kg | | Sikalastic® Rapid Catalyst | 0.60kg (6 x 0.10kg) | | Total | 10.60kg |
Please see Curing Details section for more information
Colour
Pigmented - RAL 7032 (Pebble Grey)
|
Application Information
Ambient Air Temperature
-5°C min / + 35°C max
Relative Air Humidity
The relative humidity must be ≤90%
Dew Point
Beware of condensation. Surface temperature during application and cure must be a minimum of 3°C above dew point.
The substrate temperature must not be less than +3°C if a topping is applied to the surface. Reaction problems can occur at lower temperatures.
Substrate Temperature
+3°C min / + 50°C max
Substrate Moisture Content
The surface to be coated must be dry and ice-free
The surface must be protected from moisture until the coating has hardened
Pot Life
The material in opened containers should be applied immediately.
At 20°C, 2% catalyst the pot life is approximately 15 minutes
Applied Product Ready for Use
| Temperature | Catalyst | Rain resistant | Can be trafficked/overcoated | Full cure | | 20°C | 2% | 30 minutes | 45 minutes | 3 hours |
Note: Times are approximate and will be affected by changing ambient conditions.
Higher temperatures or greater proportions of Sikalastic® Rapid Catalyst will reduce reaction times, while lower temperatures and smaller proportions of Catalyst will increase reaction times.
The following table indicates the recommended amount of Sikalastic® Rapid Catalyst required to adjust the curing reaction to the temperature.
Substrate temperature in °C; required amounts of Sikalastic® Rapid Catalyst in % w/w (guide)
| -10 | -5 | +3 | 5 | 10 | | - | - | 4% | 4% | 4% |
| 15 | 20 | 25 | 30 | 35 | | 2% | 2% | 2% | 2% | 2% |
Return-to-service times are provided as a guide only and may vary as a result of conditions. Newly installed balconies should be protected from exposure to heavy traffic by overlaying with an appropriate protective covering. This is particularly critical where early access is needed by other construction related traffic. Sika Liquid Plastics will not be held responsible for damage to balcony surfaces that results from failures to adequately protect newly laid areas.
For further advice, consult Sika Liquid Plastics Technical Customer Services
|
The above design is only a sample of the options available, for reference purposes only. Our policy of continuous improvement may result in a change of specifications without notice. If any discrepencies might be between the data sheet values and standards, we reserve the rights to make technical changes. Our company will not be held responsible, as all or any of pictures, drawings, weights and dimensions details or other elements in this document are only indicative and must not be considered contractual. Contact our sales team for other specifications or custom made products.
Contact our sales team for other specifications or custom made products.