  2. Sikacrete-213 F, Sprayable fire protection mortar, Interior & Exterior, Grey Powder, 9 kg
Sikacrete-213 F, Sprayable fire protection mortar, Interior & Exterior, Grey Powder, 9 kg

Sikacrete-213 F, Sprayable fire protection mortar, Interior & Exterior, Grey Powder, 9 kg

Cement & Mortar
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17678/image_1920?unique=ab4a244
You have already submitted a query for this product today.

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 9 kg
Usage Fire protection of concrete and reinforced concrete structures, lightweight rendering and plastering mortar
Usage Area Interior & Exterior
Color Grey powder
Chemical Base Portland cement, additives and phyllosilicate aggregates
Storage Conditions +5 °C to +30 °C - Store in original, unopened, undamaged packaging in dry conditions. Always refer to packaging
Density 2300 kg/m³
Application Thickness 10 mm >< 40 mm
Ambient Air Temperature +5°C >< +30°C
Substrate Temperature +5°C >< +30°C
Working time N/A
Waiting Time N/A
Consumption 5–6 kg/m² / 10 mm

Wet sprayed fire protection mortar

Sikacrete-213 F is a one-part, cementitious, fire protection mortar for wet spray or hand application. Suitable for fire protecting all types of reinforced concrete buildings and civil engineering structures including tunnels. It contains phyllosilicate aggregates, which are highly effective in resisting the heat of hydrocarbon fires. The fire protection performance allows a reduced thickness of fire protection required compared to concrete. The fire protection layer thickness depends on the specified fire resistance.

  • Pre-bagged dry mortar mix.
  • Application by the wet spray process or by hand.
  • Minimal layer thickness to comply with fire regulations.
  • Does not contribute to the formation of smoke or toxic fumes during a fire.
  • Lightweight, low density.
  • Easily surface finished by trowel or wooden float.
  • >240 minutes fire resistance achievable.
  • Minimal rebound.
Usage
  • Fire protection of concrete and reinforced concrete structures exposed to fire risk.
  • Fire protection of concrete member reinforced with FRP (e.g. Sika CarboDur and SikaWrap).
  • Factory made lightweight (LW) rendering and plastering mortar intended for interior and exterior use in walls, ceilings, columns and partitions as per EN 998-1. 
 
Advantages
  • Pre-bagged dry mortar mix.
  • Application by the wet spray process or by hand. 
  • Minimal layer thickness to comply with fire regulations.
  • Does not contribute to the formation of smoke or toxic fumes during a fire.
  • Lightweight, low density.
  • Easily surface finished by trowel or wooden float.
  • >240 minutes fire resistance achievable.
  • Minimal rebound.
Packaging

9 kg bag

Refer to current price list for packaging variations
Colour

Grey powder
Technical Information
Compressive Strength

~1,5 N/mm2

(EN 1015-12)

Tensile adhesion strength

≥ 0,25 MPa

Thermal Conductivity

λ10, dry,mat ≈ 0,14 W/m·K

Thermal conductivity of the material at an average temperature of 10 °C in dry state, table A.12 50 % fractile value

                      (EN 1745)

Water Absorption

Wc0

(EN 1015-18)

Diffusion Resistance to Water Vapour

µ ≤ 6

Freeze Thaw De-Icing Salt Resistance

To be resistant to frost, freeze-thaw cycles and de-icing salts, the surface of the mortar must be treated with Sikagard Wallcoat T.

Reaction to Fire

Euroclass A1
Application Information
Mixing Ratio

8 – 10 L of water per 9 kg bag
Layer Thickness

Minimum: 10 mm

Maximum: 40 mm (per layer)
Ambient Air Temperature

5 °C min. / 30 °C max.
Substrate Temperature

5 °C min. / 30 °C max.