  2. SikaForce-100 CT14, 1-Component Panel Bonding Adhesive, Interior & Exterior, Brown, 5 kg
SikaForce-100 CT14, 1-Component Panel Bonding Adhesive, Interior & Exterior, Brown, 5 kg

SikaForce-100 CT14, 1-Component Panel Bonding Adhesive, Interior & Exterior, Brown, 5 kg

Adhesives & Sealants
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17628/image_1920?unique=ab4a244
You have already submitted a query for this product today.

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 5 kg
Usage Sandwich Panels (Automated Bonding)
Usage Area Interior & Exterior
Color Brown
Chemical Base Polyurethane
Storage Conditions +5 °C to +30 °C - Store in original, unopened, undamaged packaging in dry conditions. Always refer to packaging.
Density 1.11 g/cm3
Service Temperature N/A
Application Time 5 min.
Curing Time 14 hours
Application Thickness N/A
Application Method Manual
UV Resistant No
Moisture Resistant Yes
Mold Resistant N/A
Paintable No
Sealant No
Flexible Yes

1-component adhesive for panel bonding

SikaForce-100 CT14 is a foaming, moisture curing 1-component polyurethane adhesive for bonding sandwich panels and similar constructions of various materials.  

  • Good strength at low coat weights
  • Highly foaming, expands to fill gaps and to reinforce
  • Better utilization, low waste remaining in packaging
  • Easily processed, can be pumped easily
  • Solvent free
PRODUCT BENEFITS
  • Good strength at low coat weights
  • Highly foaming, expands to fill gaps and to reinforce
  • Better utilization, low waste remaining in packaging
  • Easily processed, can be pumped easily
  • Solvent free
 
Usage
SikaForce-100 CT14 is used primarily for bonding sandwich panels with skin materials of pre-treated or primed aluminum, steel, glass fibre reinforced plastic and core materials of plywood, wood, extruded / expanded polystyrene and mineral wool. SikaForce-100 CT14 is well suited for automatic applications. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed, ensuring adhesion and material compatibility.  
Typical Product Data
Chemical base

Polyurethane

Colour (CQP001-1)

Brown

Cure mechanism

Moisture curing

Density (uncured)

1.11 g/cm3

Consistency

Liquid

Solid content

100 %

Viscosity (CQP029-4)Rheometer, PP25, shear rate 10 s-1, d=1 mm

6 200 mPa∙s A

Application temperature

15 – 30 °C

Open time (CQP591-1)

5 minutes A

Curing time (CQP591-1)

14 minutes A

Gross calorific potential (EN ISO 1716)

29.8 MJ/kg

Shelf life

12 months

CQP = Corporate Quality ProcedureA)23 °C / 50 % r.h.
Technical Information
CURE MECHANISM

The curing of SikaForce-100 CT14 takes place by chemical reaction between the adhesive and moisture. Higher temperatures speed up the curing process and lower slow it down.

CHEMICAL RESISTANCE

In case of chemical or thermal exposure, conduct project related testing.
Application Information
Surface Preparation

Surfaces must be clean, dry and free from grease, oil, dust and contaminants. After the cleaning process, a physical or chemical pre-treatment might be required, depending on surface and type of material. The type of pre-treatment must be determined by tests.
During the curing process, carbon dioxide is released from the adhesive. If none of the substrates are porous, measures need to be taken to allow the carbon dioxide to escape.
Application

Typically a coat weight between 100 g/m2 and 300 g/m2 is applied, depending on the substrates to be bonded. The specific coat weight for a given substrate combination must be determined by tests.
SikaForce-100 CT14 is a moisture curing adhesive. A water mist of approx. 10 % of the adhesive coat weight, sprayed either on the adhesive or the bond face, is required.

To prevent curing of the product in the short term, the dosage nozzles for 1-component polyurethane adhesive are typically submerged in a tray filled with SikaForce-097 Nozzle Oil, when not in use.
For manual application, apply with trowel, spray water mist on the surface and press parts together before the end of the open time.
For support on selecting and setting up a suitable pump system, contact System Engineering Department of Sika Industry.

 
Pressing

An adequate bonding pressure is necessary to obtain a voidless contact between the substrates and the adhesive. The specific pressure is, however, dependent on the core material and must be determined by tests. The pressure must always be below the maximum compressive strength of the core. After starting the press process, do not release the pressure until the press time has elapsed.
Removal

Uncured SikaForce-100 CT14 may be removed from tools and equipment with SikaForce-096 Cleaner. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.
STORAGE CONDITIONS

SikaForce-100 CT14 has to be kept between 10 °C and 30 °C in a dry place. Do not expose it to direct sunlight or frost. After opening of the packaging, the content has to be protected against humidity.