  2. SikaCem-133 Rapid Gunite, Fast-spray concrete for quick small repairs, Interior & Exterior, Grey Powder, 25 kg
SikaCem-133 Rapid Gunite, Fast-spray concrete for quick small repairs, Interior & Exterior, Grey Powder, 25 kg

SikaCem-133 Rapid Gunite, Fast-spray concrete for quick small repairs, Interior & Exterior, Grey Powder, 25 kg

Cement & Mortar
SIKA

Sika is a global leader in specialty chemicals for the construction and industrial sectors. The company develops and supplies innovative products and systems for bonding, sealing, damping, reinforcing, and protecting structures. With a strong focus on sustainability and performance, Sika serves a wide range of applications including concrete production, waterproofing, roofing, flooring, and structural strengthening.

Read more
https://www.polytrade.global/web/image/product.template/17677/image_1920?unique=ab4a244
You have already submitted a query for this product today.

This combination does not exist.

Contact Us
Preview TDS
Download TDS
General Specifications
Packaging 25 kg
Usage Large volume repairs for bridges, marine structures, tunnels, buildings, fire damaged structures
Usage Area Interior & Exterior
Color Grey powder
Chemical Base Portland cement, polymer redispersable powder, selected aggregates, silica fume and additives
Storage Conditions Store properly in original unopened, sealed and undamaged packaging in dry and cool conditions
Density 2.0 kg/L
Application Thickness 15 mm >< 150 mm
Ambient Air Temperature +3°C >< +30°C
Substrate Temperature +3°C >< +30°C
Working time N/A
Waiting Time N/A
Consumption 2.2–2.3 kg/m²/mm

R4 FAST SETTING DRY SPRAYED MICRO REPAIR CONCRETE

SikaCem-133 Rapid Gunite is a cement based, polymer modified one component fast setting repair mortar containing silica fume and high range water-reducing agents, meeting the requirements of Class R4 of EN 1504-3. Formulated for machine applications using the dry spray process with set accelerators.

Usage
▪ Large volume repairs.
▪ Bridges.
▪ Marine structures.
▪ Tunnels.
▪ Buildings.
▪ Fire damaged structures.
▪ For exterior and interior use.
▪ In place of R1, R2 and R3 mortars.  
Advantages
▪ One component, ready to use.
▪ Non silica aggregates.
▪ Low rebound losses and dust formation during the spraying process.
▪ Layer thicknesses in one application overhead up to 100mm are possible.
▪ Rapid strength gain.
▪ Fast Initial and final set times.
Packaging

25 kg bag
Colour

Grey powder
Technical Information
Compressive Strength

1 day~35MPa     
3 days~45MPa
7 days~50MPa  
28 days~60MPa    

Modulus of Elasticity in Compression

~33 GPa

(EN 13412: 2006)

Flexural Strength

~8-9MPa at 28 days

Tensile adhesion strength

~2.0MPa

(EN 1542:1999)

Coefficient of Thermal Expansion

13.5 × 10-6/°C

(EN 1770:1998)

Electrical Resistivity

~16 KΩ/cm

(4 point wenner @ 28 days)

Capillary Absorption

~0.36 kg.m-2.h-0.5

(EN 13057:2002)

Freeze Thaw De-Icing Salt Resistance

Good resistance with no visible change after 50 cycles

(EN 13687-1:2002)

Reaction to Fire

Euroclass A1
Application Information
Layer Thickness

15 mm min. / 150 mm (Vertical) 100mm (Overhead) max.
Ambient Air Temperature

+3°C min. / +30°C max.
Substrate Temperature

+3°C min. / +30°C max.
Initial set time

~12 mins

(EN 13294)
Final set time

~16 mins

(EN 13294)

Typical set time @ 20°C