Water-based epoxy coating with low VOC emissions Sikafloor-2510 W is a two-part, water-based, coloured epoxy resin floor coating with low emissions and low maintenance requirements. - Low VOC emissions.
- Good resistance to abrasion.
- Good resistance to specific chemicals.
- Good mechanical resistance.
- Low odour.
- Easy application.
- Low maintenance.
|
Usage The Product is used as a: - Primer or scratch coat.
- Smooth or textured roller coat.
- Self-smoothing wearing layer.
- Seal coat.
The Product is used on the following substrates: - Concrete and cementitious substrates.
Please note: - The Product may only be used by experienced professionals.
- The Product may only be used for interior applications.
Advantages - Low VOC emissions.
- Good resistance to abrasion.
- Good resistance to specific chemicals.
- Good mechanical resistance.
- Low odour.
- Easy application.
- Low maintenance.
Packaging | Part A | 13.6 kg | | Part B | 6.4 kg | | Part A + Part B | 20 kg |
Refer to the current price list for available packaging variations. Colour Part A | Coloured liquid | Part B | White liquid | Cured colour | Available in many colours | Cured appearance | Semi-gloss finish |
|
Technical Information Service Temperature IMPORTANT Simultaneous mechanical and chemical strain While the Product is exposed to temperatures up to +60 °C, simultaneous mechanical or chemical strain may cause damage to the Product. Do not expose the Product to chemical or mechanical strain at elevated temperatures:
|
Application Information Mixing Ratio Part A : Part B (by weight) | 68 : 32 |
Product Temperature Maximum | +30 °C | Minimum | +10 °C |
Ambient Air Temperature Maximum | +30 °C | Minimum | +10 °C |
Relative Air Humidity 75 % r.h. maximum Dew Point Beware of condensation. The substrate and uncured applied product must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the surface of the applied product. Low temperatures and high humidity conditions increase the probability of blooming. Substrate Temperature Maximum | +30 °C | Minimum | +10 °C |
Substrate Moisture Content | Substrate | Test Method | Moisture Content | | Cementitious substrates | Calcium carbide method (CM-method) | ≤6 % | | Anhydrite substrates | Calcium carbide method (CM-method) | ≤0.3 % |
No rising moisture (ASTM D4263, polyethylene sheet). Pot Life +10 °C | 120 minutes | +20 °C | 90 minutes | +30 °C | 30 minutes |
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity. Applied Product Ready for Use | Temperature | Foot Traffic | Light Traffic | Full Cure | | +10 °C | 48 hours | 5 days | 10 days | | +20 °C | 20 hours | 3 days | 7 days | | +30 °C | 10 hours | 2 days | 5 days |
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity. |
The above design is only a sample of the options available, for reference purposes only. Our policy of continuous improvement may result in a change of specifications without notice. If any discrepencies might be between the data sheet values and standards, we reserve the rights to make technical changes. Our company will not be held responsible, as all or any of pictures, drawings, weights and dimensions details or other elements in this document are only indicative and must not be considered contractual. Contact our sales team for other specifications or custom made products.
Contact our sales team for other specifications or custom made products.