2-component polyurethane adhesive for honeycomb sandwich panel bonding SikaForce-611 L20 is a low viscous, thermoactivated 2-component polyurethane adhesive for honeycomb sandwich panels. SikaForce-611 L20 is tested according to FTP Code system and approved according to the IMO Marine Equipment Directives. - Thermoactivated (short press time possible)
- Good wetting of honeycomb
- IMO approved
- Good strength
- Solvent free
|
PRODUCT BENEFITS - Thermoactivated (short press time possible)
- Good wetting of honeycomb
- IMO approved
- Good strength
- Solvent free
Usage SikaForce-611 L20 is used primarily for bonding of e.g. aluminum and steel in honeycomb sandwich panels. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed, ensuring adhesion and material compatibility. |
Typical Product Data| Cure mechanism | | Polyaddition | | Mixing ratio | by volumeby weight | 100 : 31 100 : 29 | | Application temperature | | 15 – 30 °C | | Pot-life (CQP536-3) | | 20 minutes B | | Open time (CQP526-3) | | 70 minutes B | | Press time (CQP590-4) | 1 MPa | 235 minutes B / 4 minutes C | | Shore D hardness (CQP023-1 / ISO 48-4) | | 77 D | | Tensile strength (CQP543-1 / ISO 527) | | 17 MPa D | | Elongation at break (CQP543-1 / ISO 527) | | 75 % D | | Tensile lap-shear strength (CQP546-1 / ISO 4587) | | 9 MPa D | | Gross calorific potential (EN ISO 1716) | | 22.0 MJ/kg |
| Component ASikaForce-611 L20 | Component BSikaForce-010 |
|
Technical Information CURE MECHANISM The curing of SikaForce-611 L20 takes place by a chemical reaction of the two components. Higher temperatures speed up the curing process and lower slow it down.
CHEMICAL RESISTANCE In case of chemical or thermal exposure, conduct project related testing.
|
Application Information Surface Preparation Surfaces must be clean, dry and free from grease, oil, dust and contaminants. After the cleaning process, a physical or chemical pre-treatment might be required, depending on surface and type of material. The type of pre-treatment must be determined by tests. Application Typically a coat weight between 150 and 350 g/m2 is applied, depending on the substrates to be bonded. The specific coat weight for a given substrate combination must be determined by tests.
The procedure for manual application is as follows: Ensure that the A-component is stirred thoroughly to avoid any sediment or separation, taking care not to stir too vigorously as this may introduce air into the product. Add the B-component in the specified ratio and stir thoroughly, ensuring a homogeneous mixture is achieved. Apply before reaching half of the pot-life and join parts together within the open time. Due to the capilar effect of the product, we recommend to join the parts within 10 minutes after application, for optimal strength. Consider that, if mixed in larger amounts, the exothermic reaction can reduce the pot-life and open time significantly.
For automated applications, contact the System Engineering Department of Sika Industry. Pressing An adequate bonding pressure is necessary to obtain a good contact between the substrates and the adhesive. The specific pressure is, however, dependent on the core material and must be determined by tests. The pressure must always be below the maximum compressive strength of the core. After starting the press process, do not release the pressure until the press time has elapsed. Removal Uncured SikaForce-611 L20 may be removed from tools and equipment with SikaForce-096 Cleaner. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika Cleaner-350H or a suitable industrial hand cleaner and water. Do not use solvents on skin. STORAGE CONDITIONS SikaForce-611 L20 has to be kept between 10 °C and 30 °C in a dry place. Do not expose it to direct sunlight or frost. After opening of the packaging, the content has to be protected against humidity.
The lowest allowed temperature during transportation is -20 °C for max. 7 days. |
The above design is only a sample of the options available, for reference purposes only. Our policy of continuous improvement may result in a change of specifications without notice. If any discrepencies might be between the data sheet values and standards, we reserve the rights to make technical changes. Our company will not be held responsible, as all or any of pictures, drawings, weights and dimensions details or other elements in this document are only indicative and must not be considered contractual. Contact our sales team for other specifications or custom made products.